慢应变速率法,Slow strain rate testing
1)Slow strain rate testing慢应变速率法
2)SSRT慢应变速率
1.In this paperSSRT of Bfe30-1-1 in seawater is mainly researched, andSSRT tests are adopted to evaluate the sensibility of SCC of Bfe30-1-1 in seawater.本文着重研究BFe30-1-1(焊态)材料在海水中的应力腐蚀行为,采用慢应变速率应力腐蚀试验方法,评定BFe30-1-1(焊态)材料在海水中发生应力腐蚀开裂的敏感性。
2.In this paper SCC and galvano -chemistry action in SCC of 316L、6MnR、20 Steel in H2S mediator was mainly researched, andSSRT tesls were adopted to evaluate the sensibility of SCC of 316L、16MnR、20 Steel in H2S mediator.本文着重研究316L、16MnR、20钢在H2S介质中的应力腐蚀及应力腐蚀过程中的电化学行为,采用慢应变速率应力腐蚀试验方法(SSRT),评定316L、16MnR、20在H2S介质中的应力腐蚀开裂(SCC)的敏感性,测定316L、16MnR、20在H2S介质中发生SCC时的电位变化,为在H2S介质中选用抗SCC容器用钢提供依据,同时为用电化学方法提高H2S介质中容器用钢的抗SCC性能提供依据。
英文短句/例句
1.Slow Strain Rate Test Studies of Stress Corrosion Cracking of Pipeline Steels;管线钢应力腐蚀慢应变速率拉伸试验研究
2.Stress Corossion Cracking Behavior of 5083 Aluminum Alloy in SSRT5083铝合金慢应变速率拉伸下的应力腐蚀行为
3.Evaluation of right ventricular function in patients with chronic obstructive pulmonary disease by quantitative tissue velocity imaging and strain rate imaging组织速度成像与应变率成像技术评价慢性阻塞性肺疾病患者右心室功能
4.Strain rate and stress are nonlinearly related.应变速率和应力呈非线性关系。
5.The fall in the exchange rate is slow down.汇率下跌的速度在放慢。
6.Effect of Strain Rate on Deformation Induced Ferrite Transformation of Q235 Steel应变速率对Q235钢形变诱导铁素体相变的影响
7.Study on Stimulated-scattering-induced Slow Light in a Single Mode Optical Fiber;单模光纤中受激散射效应导致的光速变慢研究
8.Influence of strain and strain rate on twin substructure of Fe-24Mn-0.5C TWIP steel应变和应变速率对Fe-24Mn-0.5C TWIP钢亚结构的影响
9.Superplasticity of TA15 Titanium Alloy Induced by Strain Rate CyclingTA15合金应变速率循环超塑性研究
10.The Research of the Power Adaptability"s Hydraulic System Based on Frequency Control变频调速功率适应型液压系统的研究
11.Strain-rate and Temperature Sensitivity Coefficient for TC11 Titanium AlloyTC11钛合金应变速率和温度敏感系数
12.The respiration rate increases slowly with temperature.呼吸速率日变化随温度的升高呈缓慢上升的趋势。
13.Simulation of DVT Technology to Improve the Electronic Efficiency of a Slow Wave Structure动态速度渐变技术提升慢波结构注波互作用效率的仿真研究
14.cause to move more slowly or operate at a slower rate.使行动更慢或在一个较慢的速率运行。
15.The Study of the Left Atrial Functions with Congestive Heart Failure by Strain/Strain Rate Imaging应变/应变率成像评价慢性心力衰竭左心房功能的临床研究
16.Effect of Carvedilol on Strain and Strain Rate in Rabbits with Chronic Heart Failure卡维地洛对慢性心力衰竭兔心肌应变及应变率的影响
17.Influence of Strain Rate on Grain Refinement by Plastic Deforming;应变速率对强塑性变形晶粒细化的影响
18.Deformation microstructure of AZ31B magnesium alloy under high strain rate compression高应变速率下AZ31B镁合金的压缩变形组织
相关短句/例句
SSRT慢应变速率
1.In this paperSSRT of Bfe30-1-1 in seawater is mainly researched, andSSRT tests are adopted to evaluate the sensibility of SCC of Bfe30-1-1 in seawater.本文着重研究BFe30-1-1(焊态)材料在海水中的应力腐蚀行为,采用慢应变速率应力腐蚀试验方法,评定BFe30-1-1(焊态)材料在海水中发生应力腐蚀开裂的敏感性。
2.In this paper SCC and galvano -chemistry action in SCC of 316L、6MnR、20 Steel in H2S mediator was mainly researched, andSSRT tesls were adopted to evaluate the sensibility of SCC of 316L、16MnR、20 Steel in H2S mediator.本文着重研究316L、16MnR、20钢在H2S介质中的应力腐蚀及应力腐蚀过程中的电化学行为,采用慢应变速率应力腐蚀试验方法(SSRT),评定316L、16MnR、20在H2S介质中的应力腐蚀开裂(SCC)的敏感性,测定316L、16MnR、20在H2S介质中发生SCC时的电位变化,为在H2S介质中选用抗SCC容器用钢提供依据,同时为用电化学方法提高H2S介质中容器用钢的抗SCC性能提供依据。
3)slow strain rate慢应变速率
1.By theslow strain rate testing,stress corrosion properties of welding joint of 2519 aluminum alloy were studied at 1.对两种焊接工艺焊接的板材焊缝部位取样,用慢应变速率试验方法,研究2519铝合金板材及两种焊接工艺焊接的接头,在3。
4)slow strain rate testing(SSRT)慢应变速率方法(SSRT)
5)SSRT慢应变速率拉伸
1.Stress Corrosion Cracking of polythionic acids(PSCC) of 304 SS were investigated bySSRT,SEM and metallographic analysis.采用慢应变速率拉伸试验(SSRT)、扫描电镜断口分析以及金相显微组织分析等方法对304不锈钢连多硫酸应力腐蚀开裂(PSCC)行为进行了研究。
2.The stress corrosion behavior of 304 stainless steel in the solution saturated by H2S and the standard solution of NACE was studied with electrochemical test and slow strain rate tension(SSRT) test.用电化学测试及慢应变速率拉伸试验(SSRT)方法对304不锈钢在饱和H2S溶液和NACE标准溶液中的应力腐蚀行为进行研究。
3.Stress Corrosion cracking of acids media(PSCC) of duplex stainles steel and ferritic stainless steel were investigated bySSRT,SEM and metallographic analysis and evaluate stress corrosion cracking sensitivity of ferritic stainless steel and duplex stainless steel in acids media.采用慢应变速率拉伸试验(SSRT)、扫描电镜(SEM)断口分析以及金相显微组织分析等方法对TP405铁素体不锈钢及2205双相不锈钢在酸性介质中应力腐蚀开裂(PSCC)行为进行了研究。
6)slow strain rate tension慢应变速率拉伸
1.The stress corrosion cracking (SCC) behaviors of X80 pipeline steel in near-neutral pH solutions were studied using electrochemical potentiodynamic scanning,slow strain rate tension(SSRT) and scanning electron microscopy.采用电化学动电位扫描技术、慢应变速率拉伸(SSRT)试验和扫描电镜观察研究了X80管线钢及焊接接头在NS4溶液中的应力腐蚀行为。
2.5% NaCl solution was investigated by usingslow strain rate tension,scanning electron microscope and transmission electron microscope.通过慢应变速率拉伸测试、扫描电镜及透射电镜分析等研究了2519铝合金在T6、T8热处理状态下,在空气和3。
3.The interaction between mechanics and electrochemistry during the stress corrosion cracking (SCC) of 7075 aluminum alloy was studied usingslow strain rate tension (SSRT) technique.用慢应变速率拉伸(SSRT)技术研究了7075铝合金在应力腐蚀过程中的力学与电化学交互作用。
延伸阅读
慢应变速率试验分子式：CAS号：性质：一种快速的测定应力腐蚀破裂性能的试验方法。在恒应变速率机上缓慢匀速地将试样拉伸（试样在试验溶液中）直至拉断为止。试验后用扫描电镜分析断口形貌。试验过程中测定载荷一延伸率曲线，从曲线可分析出很多反映应力腐蚀敏感性的参数。该法的特点是试样在预定时间内肯定会断，所以是快速。但需要专门设备——慢应变速率机。